PolyMax Tough PC-FR Black 1.75mm - 1 kg

Ref. PC03001
4.7/5

The Polymaker PolyMax PC-FR Black filament is a polycarbonate flame-retardant with UL94 V0 certification. This fire-resistant filament offers excellent resistance to high temperatures and warping.

🔖 Special offer

-15.00% instant discount with the code : POLY15

€49.55 excl. VAT
Out of stock Free shipping

💰 Your purchases with 0% tax!

Our experts are at your service to answer your questions and provide advice at info@polyfab3d.com.

Delivery within 48/72 hours

Order before 1pm. Same day shipping

Free delivery

Free delivery near you from €69.90

Premium support

Our teams are on hand to answer all your questions

Over 3500 products

A wide choice of products from the biggest brands

Use of PolyMax PC-FR Black

PolyMax PC-FR Black is a flame-retardant material that complies with the UL94 V0 standard. This filament is used in automotive, railway, and aerospace applications where mechanical stress and heat exposure are frequent.

With this high-performance polycarbonate material, your 3D prints achieve high resistance to elevated temperatures (deflection >100°C) and excellent toughness.

PolyMax PC-FR Black: key strengths

Thermal resistance: PC-FR Black is a thermally resistant and flame-retardant filament with UL94 V0 certification.

Robust filament: PolyMax PC-FR Black by Polymaker enables the printing of parts with high strength.

Print quality: PC-FR Black ensures excellent surface quality for your printed parts.

Our recommendations for PolyMax PC-FR Black

We recommend setting an extrusion temperature between 250 and 270 °C for PolyMax PC-FR Black. A print speed between 30 and 50 mm/s and a bed temperature between 90 and 105 °C are also recommended.

The use of a closed printing chamber is advised. A chamber temperature of 90 to 100 °C is recommended to thermally stabilize the material during printing. Post-print annealing for several hours is also suggested to improve performance and impact resistance.

  • 🎯 We collaborate with businesses.
  • 📦 Stock in Europe
  • 🚚 Ships within 24 hours
  • 🔐 Secure payments
  • 🔙 14 days to change your deww
  • 📱 Need advices ? Contact technical support

Specifications for PolyMax Tough PC-FR Black 1.75mm - 1 kg

Technology / Product

Technology
FDM
Material
PC
Visual Appearance
Opaque
Standards
VO
Diameter
1.75 mm
Sensitivity to humidity
Low
Application
Prototyping, Functional part
Odour
Yes
Harmful
Yes
Level of difficulty
Expert
Brand
Polymaker
Type of product
3D Filament
Colour
Black
Net weight
1 kg

Technical values

Glass transition temperature
115 °C
Deflection temperature under load (0.45 MPa)
110 °C
Deflection temperature under load (1.8 MPa)
107 °C
Temperature VICAT
116 °C
Charpy
11.7 kJ/m² of energy
Resistors
Mechanical engineering
Tensile modulus
2634 Mpa
Flexural modulus
2518 MPa
Tensile yield strength
67 MPa
Tensile strength
97 MPa
Maximum elongation at break
3.5 %
Density
1.2 g/cm3

Extrusion

Nozzle type
Brass
Type of consumable
Non-proprietary filament (open system)
Min. plateau temperature
90 °C
Max. tray temperature
105 °C
Min. extrusion temperature
250 °C
Max. extrusion temperature
270 °C
Min. speed
30 mm/s
Max. speed
50 mm/s
Minimum nozzle diameter
0.4 mm
Bowden compatibility
Yes
Warping sensitivity
Strong
Material Loader
Bambu Lab AMS, Anycubic ACE, Creality CFS, Bambu Lab AMS HT, Bambu Lab AMS Lite, Bambu Lab AMS 2 Pro, Anycubic ACE 2 Pro

Specific equipment

Closed printing enclosure
Yes
Filtration
HEPA, Coal

Installation / Prerequisites

Type
Filament on spool
Box supplied
Yes
Coil material
Plastic

Customer reviews about PolyMax Tough PC-FR Black 1.75mm - 1 kg

4/5
✓ Avis vérifié

Tested with a Bambulab X1C, is printed well apart from the deformation of the very present part during the print which slightly distorts the expected quotas and tolerances. Deformation that I usually do not find with classical PC.

Avis du 22/06/2024 par A A.
5/5
✓ Avis vérifié

good filament

Avis du 11/12/2023 par A A.
5/5
✓ Avis vérifié

very good product

Avis du 01/11/2022 par A A.

Questions des clients

Vous ne trouvez pas la réponse à votre question ?

Product added to wishlist